This paper examines the effects of fusion zone size on failure modes, static strength and energy absorption of resistance spot welds (RSW) of advanced high strength steels (AHSS). DP800 and TRIP800 spot welds are considered. The main failure modes for spot welds are nugget pull-out and interfacial fracture. Partial interfacial fracture is also observed. The critical fusion zone sizes to ensure nugget pull-out failure mode are developed for both DP800 and TRIP800 using the limit load based analytical model and the microhardness measurements of the weld cross sections. Static weld strength tests using cross-tension samples were performed on the joint populations with controlled fusion zone sizes. The resultant peak load and energy absorption levels associated with each failure mode were studied using statistical data analysis tools. The results of this study show that the conventional weld size of can not produce nugget pull-out mode for both the DP800 and TRIP800 materials.

This paper examines the effects of failure modes on the static strength and total energy absorption of aluminum spot-welded samples using experimental, statistical, and analytical approaches. The main failure modes for aluminum spot welds are nugget pullout and interfacial fracture. Two populations of aluminum spot welds were studied. Within each population, coupon configurations of lap shear, cross tension and coach peel were considered. Thirty replicate static strength tests were performed for each coupon configuration. The resulted peak load and energy absorption level associated with each failure mode was studied using statistical models. Next, an analytical model was developed to determine the failure mode of an aluminum resistance spot weld based on stress analysis. It is found that weld size, sheet thickness, and level of weld porosity and defects are the main factors determining the cross tension failure mode for an aluminum spot weld.

Tapered FRP tubes have high-energy absorption performance under axial compressive load. FRP will be useful for structural material of a shock absorber in the various industries. And in order to simulate the behavior of this material, several experimental tests and numerical simulations using FEM have been carried out recently. However, it is still difficult to simulate the behavior of tapered FRP tubes involving so called “Progressive Crushing” with FEM properly, because the fracture mechanism contains various kinds of fractures such as delamination, fiber fracture and so on. In this study, we proposed a specially designed FEM model based that is useful for the crush-worthiness analysis of FRP tube.

Single cylinder engine testing was carried out to clearly understand the test results of multi-cylinder engines reported by the Diesel WG in JCAP (Japan Clean Air Program) (1), (2), (3) and (4). In this tests, engine specifications such as fuel injection pressure, nozzle hole diameter, turbo-charging pressure, EGR rate, and fuel properties such as 1-, 2-, 3-ring aromatics content, n-,i-paraffins content, and T90 were parametrically changed and their influence on the emissions were studied. PM emission generally increased in each engine condition with increased aromatic contents and T90. In particular, multi ring aromatics brought about large increases in PM regardless of the engine conditions. The influence of fuel properties on NOx emission is smaller than the influence on PM emission. Some other fuels that have various side chain structures of 1-ring aromatics, normal paraffins only and various naphthene contents were also investigated.

This paper presents two methods of characterizing and describing the formability of tailor welded blanks (TWB). The first method involves using miniature tensile specimens, extracted from TWB weld material, to quantify mechanical properties and material imperfection within TWB welds. This technique combines statistical methods of describing material imperfection together with conventional M-K method modeling techniques to determine safe forming limit diagrams for weld material. The second method involves the use of an extended M-K method modeling technique, which places multiple material thickness and material imperfections inside one overall model of TWB performance. These methods of describing TWB formability and their application to specific aluminum TWB populations are described.

A computation tool for hydroforming prediction using an inverse approach (IA) has been developed. This approach is based on the method proposed by Guo et al. [1], however it has been extended to tube hydroforming problems in which the initial shape is not flat but is a round tube subject to internal pressure and axial feeds [2]. Although the inverse method tool is a stand-alone code, it has been linked to the Marc code for meshing purposes and visualization of results. In this paper, a finite element analysis of an extruded AA 6061-T4 tube submitted to free hydroforming conditions is carried out using the IA code. The results are in good agreement with those obtained by an incremental approach. However, the computational time in the inverse procedure is much less than that in the incremental method.

Guidelines with regard to the body strength of buses have been drawn up in Japan. We now pass to the second step in research to assure the greater safety of bus crews and passengers by launching a study on further reduction of collision injuries to bus occupants. As a way to reduce such passenger injuries, our focus is the optimization of energy absorption, the arrangement of equipment on the passenger seat back, the seat frame construction, mounting and so on. The study was conducted using an experimental method together with FEM computer simulation. The findings from a sled impact test simulating a seat in a bus in a frontal collision are stated as follows. 1.Further consideration should be given to the present conventional ELR two-point seat belt. 2.One way to reduce passenger injury is to optimize the space between seats.

This paper describes a method for predicting structural failure probabilities for automotive windshields. The predictive model is supported by the data from strength tests performed on specimens of automotive glass. Evaluations of stresses can be based on finite element calculations, or measurements of the residual stresses that arise from fabrication. Failure probabilities for each subregion of a windshield are estimated from the local state of stress, the surface area or length (for edge elements) of the subregion, and statistical distributions of glass strengths. Example calculations are presented that show the relative contributions of edge stresses, surface stresses and residual stresses to calculated failure probabilities.

A new inflator specification, the “inflator thrust variable,” was developed to better explain measured mid-sized male, instrumented test dummy responses in the chest-on-module test condition. Specifically, controlled laboratory experiments were conducted with non-production, driver airbag modules with inflators of various outputs and gas constituents in an effort to assess their effects on a pertinent occupant response. Regression analyses showed that the inflator thrust variable is a better predictor of the observed variation in peak viscous criterion responses than either peak tank pressure or the related pressure rise rate when inflators of differing gas composition were compared.

Future vehicle safety, performance and fuel economy objectives make the development of new materials, concepts and methods of crash energy management desirable. The technique of foam filling structural rails for increased energy absorption was investigated as one such concept. A fractional factorial test program was established to evaluate the weight effectiveness of polyurethane foam as an energy absorber and stabilizer. The experiment provided the quantitative effects of design parameter, varability of results and statistical significance of each parameter with regard to crash characteristics. High density foam was found to be weight effective as a structural reinforcement, but not as an energy absorber. Medium density foam improves the energy absorption of a section. Equivalent energy, however, can be absorbed more weight effectively by changing the metal thickness or the section size.

Since statistics indicate that front impact is the major accident type, Ford has been studying energy-absorbing structures for some time. Early designs such as the “ball and tube” and “rail splitter” were discarded in favor of the “S” frame. Details of the design approach and testing are given in this paper. Design objectives were increased effective collapse distance, compatibility with production practices, and maintenance of satisfactory noise, vibration, and harshness levels. Safety objectives are improved passenger compartment integrity and reduction of seat belt loads. Barrier crash tests at 30 mph (equivalent to collision into standing vehicle at 50 mph) were used to evaluate the design of the “S” frame. Results of testing indicate that occupant restraint with seat belts, combined with front end structural improvements, offer the most promise for injury reduction during service front impact accidents.